Title of article :
Microwave sintering of nanocrystalline Ytzp (3 Mol%)
Carmen Garc?´a-Gan? a´n، نويسنده , , Juan Jose´ Mele´ndez-Mart?´nez، نويسنده , ,
Diego Go´ mez-Garc?´a، نويسنده , , Arturo Dom?´nguez-Rodr?´guez، نويسنده ,
Issue Information :
دوهفته نامه با شماره پیاپی سال 2006
Microwave sintering of nanophase Y2O3–
ZrO2 (3 mol%), 3-YTZP, to near theoretical density was
achieved using a multimode cavity furnace at 2.45 GHz.
Sintering is discussed briefly and compared with the
conventional sintering process reported in literature.
Different characterization techniques have been performed,
showing that a small and uniform nanograin
structure was developed in fully dense sintered samples.
The average grain size of the microwave-sintered specimens,
less than 50 nm, was measured, and the creep
behaviour of the samples was studied at temperatures
between 1,050 C and 1,150 C.
Journal title :
Journal of Materials Science