Title of article :
Cyclic fatigue resistance of 2Shape, Twisted File and EndoSequence Xpress nickel-titanium rotary files at intracanal temperature
Author/Authors :
Uslu ، Gülşah - Çanakkale Onkekiz Mart University , Özyürek ، Taha - Ondokuz Mayıs University , Gündoğar ، Mustafa - Medipol University , Yılmaz ، Koray - Hatay Mustafa Kemal University
Pages :
5
From page :
283
To page :
287
Abstract :
Background. The aim of this study was to compare the cyclic fatigue resistance of 2Shape, Twisted File (TF) and EndoSe-quence Xpress (ESX) nickel-titanium rotary files at intracanal temperature (35°C). Methods. Twenty 2Shape TS1 (25/.04), 20 TF (25/.04) and 20 ESX (25/.04) files were tested for cyclic fatigue at intracanal temperature (35°C). All the instruments were rotated in artificial canals which were made of stainless steel with an inner diameter of 1.5 mm, 60° angle of curvature and a radius curvature of 5 mm until fracture occurred; the time to fracture was recorded in seconds using a digital chronometer and the number of cycles to fracture (NCF) for each file was calculated. Kruskal-Wallis test with Bonferroni correction was performed to statistically analyze data using SPSS 21.0. Statistical significance was set at P 0.05. Results. NCF values revealed that the 2Shape had significantly the highest cyclic fatigue resistance, followed by TF and ESX at intracanal temperature (P 0.05). The difference was significant between the TF and ESX groups (P 0.05). There was no significant difference among the 2Shape, TF and ESX files with respect to the lengths of the fractured file fragments (P 0.05). Conclusion. Within the limitations of present study, it was concluded that the cyclic fatigue resistance of 2Shape files at the intracanal temperature is higher than that of TF and ESX files.
Keywords :
Cyclic fatigue , EndoSequence Xpress , Twisted File , 2Shape , static test