Fibrous mixed conducting cathode with embedded ionic conducting particles for solid oxide fuel cells
Author/Authors :
Choi، نويسنده , , Jinyi and Kim، نويسنده , , Byeongseok and Shin، نويسنده , , Dongwook، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2014
Pages :
6
From page :
14460
To page :
14465
Abstract :
The Sm0.5Sr0.5CoO3−δ (SSC) fibers with embedded nano-Sm0.2Ce0.8O1.9 (SDC) particles are fabricated by electrospinning process using commercial SDC nanopowders and an SSC precursor gel containing polyvinyl alcohol (PVA) and aqueous metal nitrate. After calcination at 800 °C, fibers with diameters ranged between 300 and 500 nm and well-developed SSC cubic-perovskite structure and SDC fluorite are successfully obtained. The calculated crystallite sizes of SSC and SDC are 20.78 and 45.35 nm, respectively. Over whole measured temperature ranges during the symmetrical cell test, the fiber composite cathode exhibits much lower polarization resistance than conventional powder composite cathodes. The polarization resistances are estimated to 0.06 and 1.23 Ω cm2 for the fiber composites and 0.15 and 2.10 Ω cm2 for the powder composites at 700 and 550 °C, respectively. The single cell with the fiber composite cathode shows much higher performances; its maximum power density is 380.5 mW cm−2 at 550 °C and higher than 1278 mW cm−2 at 700 °C.
Keywords :
Composite cathode , One-dimensional structure , Ceramic fibers , solid oxide fuel cells