Growth of intermetallic layer in the aluminide mild steel during hot-dipping
Author/Authors :
Cheng، نويسنده , , Wei-Jen and Wang، نويسنده , , Chaur-Jeng، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2009
Pages :
5
From page :
824
To page :
828
Abstract :
Mild steel was coated by hot-dipping in a molten aluminum bath. The growth behavior in the intermetallic layer after various times of immersion in the hot-dip at 700 °C was analyzed by electron backscatter diffraction (EBSD). The results showed that the aluminide layer consisted of an outer aluminum topcoat, minor FeAl3 and major Fe2Al5, respectively. From another perspective, Fe2Al5 possessed a tongue-like morphology, which caused the corresponding serration-like morphology of the steel substrate. The Fe–Al/steel substrate interface of the Fe2Al5 phase, after removal of the steel substrate, displayed a columnar structure growing toward the steel substrate, implying that Fe2Al5 grew at a rapid rate along the diffusion direction. Moreover, the EBSD results revealed the Fe2Al5 phase was not only composed of columnar grains, but also possessed fine grains clustered around the peaks of the serration-like steel substrate.
Keywords :
Tongue-like morphology , Mild steel , intermetallic layer , Hot-dipping , EBSD
Journal title :
Surface and Coatings Technology
Journal title :
Surface and Coatings Technology
Serial Year :
2009
Link To Document :
بازگشت