Microstructural evolution of YSZ electrolyte aerosol-deposited on porous NiO-YSZ
Author/Authors :
Choi، نويسنده , , Jong-Jin and Choi، نويسنده , , Joon-Hwan and Ryu، نويسنده , , Jungho and Hahn، نويسنده , , Byung-Dong and Kim، نويسنده , , Jong-Woo and Ahn، نويسنده , , Cheol-Woo and Yoon، نويسنده , , Woon-Ha and Park، نويسنده , , Dong-Soo، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2012
Pages :
6
From page :
3249
To page :
3254
Abstract :
Dense, crack-free, ∼7.5 μm thick, 8 mol% yttria stabilized zirconia (YSZ) film was aerosol deposited on porous NiO-YSZ anode substrates at room temperature without additional high-temperature sintering. The films’ microstructures and gas permeability were observed after annealing at various temperatures. The dense, gas-tight film that was observed up to 1000 °C became porous at higher temperatures probably due to structural instability related to oxygen non-stoichiometry. A cell using such film as electrolyte showed an open cell voltage of 1.10 V and a maximum power density of 0.51 W/cm2 at 750 °C.
Keywords :
Microstructure-final , grain size , ZrO2 , Fuel cells , Aerosol deposition