Reversible α′ ↔ β′ transformation in a textured Sm-sialon ceramic
Author/Authors :
Carman، نويسنده , , Andrew and Pereloma، نويسنده , , Elena and Cheng، نويسنده , , Yi-Bing، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2011
Pages :
11
From page :
1165
To page :
1175
Abstract :
A preferential orientation was observed in a Sm-sialon ceramic, of the composition Sm0.4Si9.6Al2.4O1.2N14.8, after hot pressing at 1800 °C for 2 h. Post-sintering heat treatment was performed at 1450 °C for 384 h, resulting in the forward α′ → β′ transformation, accompanied by the formation of M ′ SS and an increase in the 21R phase. Subsequent heat treatment at 1800 °C for 2 h resulted in the reverse β′ → α′ transformation, with a corresponding decrease in the M ′ SS and 21R phases. This confirms the fully reversible reaction of α ′ + liquid ↔ β ′ + M ′ SS + 21 R in Sm-sialon ceramics. In addition, the texture introduced by hot pressing was maintained after all heat treatments, indicating that there is a crystallographic relationship between the transformation phases. The microstructure and mechanical properties were also found to be mostly reversible, contrary to the behaviour of the α′ lattice parameters and bulk density.
Keywords :
Sialon , HOT PRESSING , mechanical properties , Transformation cycling , Microstructure-final