Title of article :
Preparation and mechanical properties of large-ingot Fe3Al-based alloys
Author/Authors :
Y.D. Huang *، نويسنده , , W.Y. Yang، نويسنده , , Z.Q. Sun، نويسنده , , L Froyen، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2004
Pages :
6
From page :
175
To page :
180
Abstract :
Recent improvements of room temperature ductility and high temperature strength have shown that Fe3Al-based alloys could start their cut-and-try commercial applications in industry. This paper presents the results on development of large-ingot Fe3Al-based alloys, including melting, thermomechanical processing and mechanical properties. A large ingot weighing 269 kg, with a high quality surface was fabricated by vacuum induction melting. Conventional thermomechanical processes were used to produce bars, sheets and seamless tubes. By controlling the thermomechanical treatment, a room temperature ductility with a value of more than 10% was achieved which is only a little lower than that prepared in the laboratory. The creep lifetime at 600 °C and 200 MPa was more than 2000 h after annealing.
Keywords :
Thermomechanical process , Vacuum induction melting , Mechanical properties , Iron aluminide , Intermetallics
Journal title :
Journal of Materials Processing Technology
Serial Year :
2004
Link To Document :
بازگشت