Title of article :
Effect of semisolid microstructure on solidified phase content in 1xxx Al alloys Original Research Article
Author/Authors :
C.M Allen، نويسنده , , K.A.Q OʹReilly، نويسنده , , B Cantor، نويسنده ,
Issue Information :
دوهفته نامه با شماره پیاپی سال 2001
Pages :
15
From page :
1549
To page :
1563
Abstract :
Melt-spun high purity Al–0.3 wt% Fe–0.1 wt% Si alloys, containing V and Al–5Ti–1B grain refiner, were melted at 2 K/min from 635°C to different temperatures above the solidus in a differential scanning calorimeter (DSC). Quenched and slow cooled (at 2 K/min) microstructures were examined using scanning electron microscopy (SEM). Melting was observed in a hot-stage reflected light microscope. Al–Fe4Al13 melted first, forming cell boundary liquid films. Rapid coarsening occurred at <4 K above the solidus via motion of these boundaries. Intracellular liquid droplets formed at 4–6 K above the solidus. These droplets have been demonstrated to be sites of metastable Al–FeAlm formation in V and Al–5Ti–1B containing alloys on solidification. With increasing temperature the liquid cell boundaries thickened and consumed the droplets, until there were none left at 10 K above the solidus, when the microstructure was fully molten. Consequently Al–FeAlm only formed in V and Al–5Ti–1B containing alloys when solidified following melting to 4–10 K above the solidus.
Keywords :
Casting , Aluminium alloys , Differential scanning calorimetry (DSC) , Microstructure , Nucleation