Effects of hot-working parameters on microstructural evolution of high nitrogen austenitic stainless steel
Author/Authors :
C.M. Hong، نويسنده , , J. Shi، نويسنده , , L.Y. Sheng، نويسنده , , W.C. Cao، نويسنده , , W.J. Hui، نويسنده , , H. Dong، نويسنده ,
Issue Information :
ماهنامه با شماره پیاپی سال 2011
Pages :
7
From page :
3711
To page :
3717
Abstract :
The microstructural evolution of high nitrogen austenitic stainless steel under various deformation conditions was characterized by isothermal compression test. Special attention was paid to the variation of microhardness and its relationship with grain size was also derived. Results indicated that two kinds of strengthening mechanism acted during the whole temperature range. When the temperature is between 950 °C and 1150 °C, grain refinement plays a dominant role. But at temperatures lower than 900 °C, no recrystallization occurs and substructure (dislocations and twins) contributes massively to the strength. Furthermore, it was found that the peak precipitation of grain boundary carbides which are seriously detrimental to toughness appeared at 850 °C. Therefore, an optimizing processing route could be recommended to achieve a good combination of high strength and good toughness. Firstly, the hot-rolling at 950–1100 °C should have large stain to gain refined grains, and accelerated cooling is applied from 950 to 750 °C in order to avoid carbide precipitation along grain boundary. Lastly, at temperatures lower than 750 °C warm-rolling with medium stain can get substructure strengthening effects.
Keywords :
F. Microstructure , A. Non-ferrous metals and alloys , H. Selection of material processes