Effect of Deposition Regime on Tribological Behavior of VK8Coating on 1.2344 Tool Steel Obtained by Electro Spark Method
Author/Authors :
آقاخاني، محسن نويسنده كارشناس ارشد-دانشگاه آزاد اسلامي واحد نجف آباد Aghakhani, Mohsen , شفيعي، علي نويسنده پژوهشکده مهندسي ژئوتکنيک-پژوهشگاه بين المللي زلزله شناسي و مهندسي زلزله shafie, ali , مناجاتي زاده، حسين نويسنده , , آقاخاني، محمد علي نويسنده كارشناس ارشد دانشگاه صنعتي اصفهان Aghakhani, Mohammad Ali
Issue Information :
فصلنامه با شماره پیاپی 2 سال 2013
Pages :
7
From page :
21
To page :
27
Abstract :
In this study, the effect of deposition regime on the wear behavior of VK8 coating applied to 1.2344 tool steel by electro spark method (ESA) was investigated. After sample preparation, the coating with high and low regime was applied. To assess the wear behavior, the pin on disk test method according to ASTM G99-04, was used. For surveying surface morphology and cross section of the coating as well as the substrate, optical microscope and SEM were used. Also for phase evaluation of the coating, X-ray diffraction (XRD) was used. The results show that the imposed regime is very impressive on the thickness of coating and wear resistance. In low regime, less porosity, better finishing surface and lower coating thickness was achieved. In this regime, better wear resistance was obtained.
Journal title :
Journal of Advanced Materials and Processing
Link To Document :