Effect of excess Pb on crystallinity and ferroelectric properties of PZT(40/60) films on LaNiO3 coated Si substrates by MOD technique
Author/Authors :
J.H. Ma*، نويسنده , , XJ Meng، نويسنده , , J.L. Sun، نويسنده , , T. Lin، نويسنده , , F.W. Shi، نويسنده , , G.S. Wang، نويسنده , , J.H. Chu، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2005
Pages :
5
From page :
275
To page :
279
Abstract :
Pb(Zr0.4Ti0.6)O3 [PZT(40/60)] films were deposited onto LaNiO3 (LNO) coated Si substrates by metal-organic decomposition (MOD) technique. Excess Pb was incorporated in the film by using excess Pb (2%–15%) in the solution. The crystallinity and ferroelectric properties of PZT films were investigated by using X-ray diffraction (XRD), RT66A test system and HP4194 impedance analyzer, respectively. Rayleigh law was employed to analyze the defect concentration in the films. The results show that all the PZT films show the (1 0 0) preferential orientation with complete perovskite structure except for the 2% film displaying some pyrochlore phase. The (1 0 0) preferential orientation is mainly attributed to LNO bottom electrode, which has the highly (1 0 0) preferential orientation. The 10% film shows the best polarization and dielectric properties. The remnant polarization and coercive field are about 10.1 mC/cm2 and 73 kV/cm under an electric field around 330 kV/cm, respectively. And the dielectric constant and dissipation factor are about 656 and 0.022 at a frequency of 1 kHz, respectively. The good ferroelectric properties of the 10% film are mainly attributed to the low defect concentration in the film.
Keywords :
PZT thin films , Excess Pb , Ferroelectric properties , Crystallinity
Journal title :
Applied Surface Science
Journal title :
Applied Surface Science
Serial Year :
2005
Link To Document :
بازگشت