Title of article :
Infrared spectroscopic studies on Mg intercalated crystalline MoO3 thin films
Author/Authors :
Tarsame S. Sian، نويسنده , , G.B. Reddy، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2004
Pages :
5
From page :
1
To page :
5
Abstract :
MoO3 thin films were intercalated with Mg ions using a standard three-electrode configuration. The concentration of Mg ions was varied from x ¼ 0:05 to x ¼ 0:4, where x is the ratio of Mg ions and host Mo ions. IR studies were carried out on unintercalated, intercalated, deintercalated and aged films. The effect of ion concentration (x) on lattice distortion and reversibility has been investigated by monitoring systematically the number of resonance absorption peaks, their respective intensities and spectral locations. At low values of x (<0.2) the lattice expansion along b-axis was observed and beyond which lattice distortion along a-axis was seen. The presence of characteristic resonance absorption peaks at 988, 808 and 537 cm 1 confirms formation of layered orthorhombic MoO3 phase. IR studies of deintercalated films confirm that the chemical changes occurring at terminal double bonds are irreversible while these are reversible at other sites. The stability of intercalated films was investigated by monitoring the IR reflectance time to time after exposing them to ambience. No measurable degradation was observed even after 6 months.
Keywords :
Electrochromic device , Intercalated , Deintercalated , Lattice distortion and Colored state stability
Journal title :
Applied Surface Science
Journal title :
Applied Surface Science
Serial Year :
2004
Link To Document :
بازگشت